常用高强钢材质有哪些？

牌号

C

Si

Mn

P

S

Q420B

≤0.2

≤0.55

≤1.7

≤0.035

≤0.035

Q460C

≤0.2

≤0.55

≤1.8

≤0.030

≤0.030

Q550D

≤0.18

≤0.6

≤1.8

≤0.030

≤0.025

Q690D

≤0.18

≤0.6

≤2.0

≤0.030

≤0.025

Q890D

≤0.2

≤0.8

≤2.0

≤0.020

≤0.010

Q960E

≤0.2

≤0.8

≤2.0

≤0.020

≤0.010

牌号

抗拉实验（厚度≤16mm）

横向夏比V型冲击10*10*55mm

180°冷弯实验弯芯直径

屈服强度

抗拉强度

延伸率A%

温度

冲击功

Q420B

≥420Mpa

520-680Mpa

≥18

20℃

≥34 J

d=2a

Q460C

≥460Mpa

550-720Mpa

≥17

0℃

≥34 J

d=2a

Q550D

≥550Mpa

670-830Mpa

≥17

-20℃

≥27 J

d=2a

Q690D

≥690Mpa

770-940Mpa

≥14

-20℃

≥27 J

d=2a

Q890D

≥890Mpa

940-1100Mpa

≥11

-20℃

≥34 J

—

Q960E

≥960Mpa

980-1150Mpa

≥10

-40℃

≥27 J

—